菠萝叶纤维制备纳米纤维素晶体的研究
陈红莲 高天明 郑龙 廖建和 黄茂芳Preparation of Nano-crystalline Cellulose from Pineapple Leaf Fiber
CHEN Honglian GAO Tianming ZHENG Long LIAO Jianhe HUANG MaofangAuthor information+
文章历史+
菠萝叶纤维经过氢氧化钠预处理、硫酸水解制备得到纳米纤维素晶体（NCC），再用扫描电镜（SEM）、傅立叶转换红外光谱仪（FTIR）、热重（TG）分析仪和X-射线衍射分析仪（XRD）对其结构和性能进行表征和分析。结果表明，NCC晶体颗粒尺寸为30~50 nm；红外光谱证明非纤维素部分有效去除；NCC晶型仍属于纤维素I，结晶度从75.9％提高到87.5％；比起原纤维，NCC的降解温度明显降低。
Abstract
Pineapple leaf fiber（PALF）was pretreated by sodium hydroxide, and hydrolyzed by sulfuric acid, then the nano-crystalline cellulose（NCC）was gotten. We characterized the structure and properties of NCC by SEM, FTIR, TG and XRD. The results showed that the size of NCC is 30～50 nm, non-cellulose was eliminated effectively, crystalline cellulose type of NCC is cellulose I, degree of crystallinity rises from 75.9% to 87.5%, and compared to the original fiber, the degradation temperature decreases clearly.
关键词
菠萝叶纤维 /纳米纤维素晶体 /制备 /表征{{custom_keyword}} /
Key words
Pineapple leaf fiber /Nano-crystalline cellulose /Preparation /Characterization{{custom_keyword}} /
引用本文
导出引用
陈红莲 高天明 郑龙 廖建和 黄茂芳.菠萝叶纤维制备纳米纤维素晶体的研究[J]. 热带作物学报, 2012, 33(1): 153-156
CHEN Honglian GAO Tianming ZHENG Long LIAO Jianhe HUANG Maofang.Preparation of Nano-crystalline Cellulose from Pineapple Leaf Fiber[J]. Chinese Journal of Tropical Crops, 2012, 33(1): 153-156
PDF(319 KB)
448
Accesses
0
Citation
Detail
段落导航
相关文章
摘要Abstract关键词Key words引用本文相关知识
纤维素纳米纤维可控制备及其宏观组装研究取得进展
纳米纤维素：未来材料的绿色革命
基于一维CuO、ZnO纳米纤维的复合材料的制备及气敏性能研究
前景广阔的膳食纤维
天然可再生资源——木质材料的纳米科技
如何制备粒状、管状、片状、花状、空心球状的纳米氧化铝？
叶纤维
木聚糖基抗氧化活性包装膜的制备及性能研究.pdf
改性纤维素材料对金属离子吸附研究进展
一文了解不同形貌纳米勃姆石的制备方法
网址: 菠萝叶纤维制备纳米纤维素晶体的研究 https://m.huajiangbk.com/newsview2467985.html
| 上一篇: 科学家用回收的菠萝叶制成气凝胶 |
下一篇: 开花无叶的是什么花 不开花的绿植 |